The product is a translucent to transparent paste-like, non-flowing, two-component thixotrope. It consists of a modified polyamine curing agent and epoxy resin as the main agent of the product

It is mainly used in the stone processing industry to enhance the natural stone and concrete with large holes and cracks, and to improve the surface quality and the yield and benefit of the stone. Can also be used for bonding vertical surfaces. Due to its thixotropy, it is also suitable for bonding hard PVC, polystyrene, polyurethane, steel, iron, wood, etc. The materials that cannot be bonded are polyethylene, polypropylene, Teflon, etc.

1. the bonding parts of the rough grinding, and remove the stone surface of the oil, dust and other pollutants, in order to keep the surface clean and dry
2. Preheating the stone surface can speed up the curing speed and improve the mechanical propertiesof the cured material.
3. Proportion (weight ratio) A 2 parts, B 1 part. After weighing, it should be thoroughly mixed until the color of the mixture is consistent. If necessary, add Kodak color paste for color mixing, up to 5%
4. the mixture can work for 15-20 minutes (25 degrees C), with a scraper. Repeat operationfor large area crack
5. After about 24 hours at room temperature (25 ℃), the treated surface can be polished and polished. If the slate is preheated to 60±5 ℃, then gluing and baking the plate, after 2 hours, the next processcan be entered.
6. Tools can be cleaned with Keda special diluent or cleaning agent
7. Increasing the temperature will accelerate the curing reaction, and lowering the temperature will delay the curing reaction
8. Before handling the empty tank, the packaging tank must be completely emptied.

1. When using this product, please wear liquid protective gloves
2. according to different stone, the treated stone surface should have different degrees of deepening
3. The bonding surface must be cleaned before construction, and the surface should be polished when it is smooth to avoid affecting the bonding strength
4. Only by ensuring the correct mixing ratio can the ideal mechanical and chemical properties be obtained. Incorrect mixing ratio will lead to unsatisfactory hardening effect
5. the construction temperature can not be lower than 5 ℃, appropriate heating in winter can speed up the curing speed and improve the bonding strength
6. The amount of glue should not be too much, and the construction should be completed within the working time; the higher the temperature, the more the amount of glue, the shorter the time that can be used, and the longerthe time that can be used.
7. This product has a long application period and must wait for the glue to be completely cured before stacking, so as not to pollute other stones
8. The blended glue is too viscous or gel, please stop using it.
9. The slate can only be polishedafter the glue is completely cured.
10. Please use different tools and containers for the two-component glue. Do not put the remaining glue solution after mixing back to the original package; Do not mix the lid of component A and component B, and do not enterit.
11. such as glue viscosity is too large, can add a small amount of ethanol or acetone dilution, or the plate for preheating after use, and the, B glue placed in the container separately in 40-80 ℃ water heating, to reduce the viscosity, in order to improve the glue permeability
12. The adhesive overflowing from the bonding part shall be cleanedwith a cloth dipped in a small amount of alcohol or acetone before curing.
13. Once hardened, the filling layer will not be dissolved and moved unless mechanical force or high temperature (>200 ℃) is used to destroy the adhesive layer.
14. the correct operation, the hardened fill layer is harmless to the body 15. When handling empty tanks, the packaging tank must be completely emptied.