The product is a liquid, solvent-free, flowing, two-component adhesive. It is composed of a modified alicyclic curing agent and epoxy resin as the main agent

Mainly used in the stone processing industry, used to strengthen the repair of stone surface cracks, small holes, sand holes, ant road, convex and concave inequality, improve its surface quality. Can also be used for glass gauze reinforced fragile slate. The product can also be used for bonding other materials such as hard PVC, steel-iron, steel-steel, ceramics, polyurethane, paper and wood. In the electronics industry can be used to seal electronic components

1. the bonding parts of the rough grinding, and remove the stone surface of the oil, dust and other pollutants, in order to keep the surface clean and dry
2. stone surface preheating can improve the permeability, curing speed, can improve the mechanical properties of cured products
3. Proportion (weight ratio) A 2 parts, B 1 part. After weighing, mix thoroughly until the color of the mixture is consistent. If necessary, add Kodar color paste for color adjustment, up to 5%
4. the mixture can work for 10-20 minutes (25 ℃), with a fine tooth scraper or wool brush. For large area cracks and strong absorption surface should be repeated many times; for small cracks, should be scraped back and forth, so that the glue liquid multiple penetration
5. After about 24 hours at room temperature (25 ℃), the treated surface can be ground and polished. If the natural stone slab is preheated to about 60 ℃, then glued, the next operation can be carried out after about 2 hours
6. Tools can be cleaned with Keda special diluent or cleaning agent
7. Increasing the temperature will accelerate the curing reaction, and lowering the temperature will delay the curing reaction
8. Before handling the empty tank, the packaging tank must be completely emptied.

1. please wear protective gloves during construction
2. Before construction, the surface must be cleaned. When used for bonding, the smooth surface should be polished to avoid affecting the bonding strength
3. glue is now in use, the amount of glue should not be too much, so as not to make the working time is too short, and affect the operation. When weighing component A and component B, different tools shall be used separately and shall not be exchanged. Please cover the lid after use
4. such as the glue has become thick or initial set, please do not use
5. Ensure the correct mixing ratio and full mixing to get good mechanical and chemical properties, otherwise, the performance will not be guaranteed or even lose its effect
6, below 10 ℃, the curing reaction is slow, should be used carefully or improve the curing temperature of the place
7. such as glue viscosity is too large can add a small amount of ethanol or acetone dilution, or will be used after preheating plate, or glue placed in 40-80 ℃ water bath heating, to reduce the viscosity, in order to improve the permeability of glue
8. Once the filling layer is hardened, it will not be dissolved unless mechanical force or high temperature (>200 ℃) is used to destroy the adhesive layer.
9. The adhesive overflowing from the bonding part shall be cleaned with a cloth dipped in a small amount of alcohol or acetone before curing.
10. The slate after glue adjustment must be placed flat. After the glue is cured and does not stick to hands, apply a proper amount of lubricant such as talcum powder on the slate, and then stack it to prevent the upper and lower stones from sticking together.
11. If the product is used correctly, the cured product is harmless to the body
12. different stone, processed stone surface will have different degrees of deepening
13. the construction site should be well ventilated, no fireworks, prevent children contact, do not enter